Plastic Plates for Single Rope Mine Hoist
|FOB Price:||US $5-200 / Piece|
|Min. Order:||1 Piece|
|Min. Order||FOB Price|
|1 Piece||US $5-200/ Piece|
|Transport Package:||Sea Worthy Packing or as Required|
|Payment Terms:||L/C, T/T|
- Material: Plastic
- Water Absorption: 0.2%~0.4%
- Origin: China
- Kind: Engineering Plastic Sheet
- Trademark: CIC
The comprehensive offering of various technologies enables virtually all types of material to be treated efficiently and profitably
CIC offers access to unparalleled expertise and experience of the industry and makes the process more efficient in rotary kiln
Lower operating costs and improved equipment efficiency, teamed up with added safety, health and environment-friendly efficiency, form the heart of the values we offer our customers
These all can create significant cost savings
1. Of high mechanical strength, and long usage cycle
The compressive strength of this kind of plastics plates is 7 to 10 times higher than that of the wood liner, thus conditions such as crushing and flatting of the wire rope groove, and its usage cycle is above 5 times longer than that of the wood liner.
2. Of wide range of application
The plastic plates are of good resistance of desiccation and moisture, avoiding the phenomenon of the sun cracking and rotting of the wood. They are especially suitable for using in severe environment, such as Mining of large water spray and high corrosivity, and underground mining.
3. Of light proportion and no water absorption
The proportion is 0.98, which is lighter than the wood liner after absorption, thus the rotational inertia and the reactive power of the equipment would not be increased.
4. Compression moulding, with flat surface of the rope groove
They are easy to install. With the neatly rank of the wire rope, phenomenon such as locking and skipping of the wire rope could be avoid from happening, and the usage life of the wire rope could be extended.
|Ware Rate (10-7cm3/Kgm)||1.0||3 times higher than that of the timber|
|Degree of Corrosion (g/m2)||≥±2||7times higher than that of the timber|
|Hardness (Shore D)||70~84|
|Martin Heat Resistance (ºC)||0~65|
|Density (g/cm3)||0.97~0.99||Generally density of the wood is 0.85|
|Impact Strength (kg.cm/cm2)||7.1~9.5|
|Compressive Strength (Mpa)||68.5||Wood horizontal grain bearing stress is 0.85|
|Bending Strength (Mpa)||61.5||Bending strength of wood is 6|
|Water Absorption (%)||0.01|